Otai Polyvinyl Chloride (PVC) waterproofing membrane is a type of new high macro-molecular waterproofing membrane by adding plasticizer , filler ,anti-oxidizer , ultraviolet light absorber and other auxiliaries with polyvinyl chloride resins as raw material.

Standard Specification

Width : 2.0m

Thickness : 1.2mm, 1.5mm. 1.8mm， 2.0mm

Length :20m

Product Features

1. High tensile strength , good elongation , strong applicability for base expansion or cracking deformation .

2. Large width ,high construction efficiency , small product consumption .

3.Good diffusion of water vapor , easy discharge of condensate , easy discharge of moisture left in the substrate

4. Root penetration resistance , chemical corrosion resistance and aging resistance ;

5. maintain good flexibility even at -25℃

6.High Security without open flame installation

7. It used for exposed ,service life 10 years ; if unexposed used , the service life can be 50-100 years .

8. The artificial weathering time of Otai PVC is not less than 4100 hours.

9.Anti-Wind reach 135 PSF

Technical Data Sheet

No.	Test Item		Index
No.	Test Item		H	L	P
1	The thickness of resin layer above the reinforcement fabric/ mm ≥		-	-	0.40
2	Tensile property	Maximum Tension N/cm ≥	-	120	250
		Tensile Strength Mpa ≥	10.0	-	-
		Max Tension Elongation/ % ≥	-	-	15
		Breaking Elongation/ %≥	200	150	-
3	Heating treatment size change rate % ≤		2.0	1.0	0.5
4	Low temperature bending		-25 ℃ No.Crack
5	Water impermeability		0.3Mpa, 2h Impermeable
6	Impact resistance		0.5kg, m ,impermeable
7	Anti-static load		-	-	20kg impermeable
8	Seam peel strength N/mm ≥		4.0	4.0	3.0
9	Right -angle tear strength N/mm ≥		50	-	-
10	Trapezoid tear strength N ≥		-	150	250
11	Water absorbing capability (70 ℃， 168h)%≤		After soaking		4.0
11	Water absorbing capability (70 ℃， 168h)%≤		After airing		-0.4
12	Heat aging (115 ℃）	Time/h	672
		Appearance	No bubble ,crack ,delamination , bonding and holes
		Max tensile retention %≥	-	85	85
		Elongation retention % ≥	85	-	-
		Tensile strength ( Max tension on )retention %≥	-	-	80
		Breaking elongation retention /%≥	80	80	-
		Cold bending	-20 ℃ No. Cracking
13	Chemical resistance	Appearance	No bubble ,crack ,delamination , bonding and holes
		Max tensile retention %≥	-	85	85
		Elongation retention % ≥	85	-	-
		Tensile strength ( Max tension on )retention %≥	-	-	80
		Breaking elongation retention /%≥	80	80	-
		Cold bending	-20 ℃ No. Cracking
14	Artificial Climate accelerating aging	Time/h	1500
		Appearance	No bubble ,crack ,delamination , bonding and holes
		Max tensile retention %≥	-	85	85
		Elongation retention % ≥	85	-	-
		Tensile strength ( Max tension )retention %≥	-	-	80
		Breaking elongation retention /%≥	80	80	-
		Cold bending	-20 ℃ No. Cracking
Single-ply roof membrane artificial climate accelerating aging time is 2500h, no exposed used membrane no need to test artificial climate accelerating aging

Certificates

CE Certificates

Scope of Application

Installation Methods& Vedio

Classic Projects Reference

Concrete Roof Mechanical Fixation Method

Metal Roof Waterproofing

Roofing Details Treatment

Self Adhesive Polymer Waterproof Membrane Application for Concrete Roof

The installation of TPO waterproofing membrane is combined with advanced and mature technology , and complete application . Hot air welding is adopted for the overlaps of membranes, and between membrane and prefabricated accessories . The Installation are basically categorized as ballasted system, full adhered system and mechanical attachment system .

Ballasted System

The membrane is installed by adhesive or metal battens at certain area .The remaining area is not attached . Overlaps is welded by hot air. The wind uplifting force is withheld by the weight of ballasted materials .

System Features

　. Suitable for all types of different substrates

　. Quick installation

　.Low Installation cost ;

　.Excellent weathering resistance

The installation method is suitable for green roofs , driving roofs , the often step roof and non-often step roofs covered with cobble stones or prefabricated blocks.

Fully -Adhered System

The TPO membrane is adhered to base with adhesive . Overlaps is welded by hot air .

System features

　. For roofs with complicated structure;

　. Light weight ;

　. Strong wind uplift resistance ;

　. Great looking

The installation method is suitable for concrete roofs and steel roofs with high density insulation boards .

Mechanical Fixation System

The roofing membrane is installed by special roofing screws with plates or battens to the basis like structural concrete ,steel deck or wooden deck ,etc. The Overlap between the seams of the membrane sheet is welded by hot air welder .

System Features

. Easy installation

. Strong wind resist

. High performance of cost ratio

. Light Weight

The installation method is suitable for concrete roofs , steel roofs , aluminum roofs .

On a

Fabric Backing PVC membrane (L)